Uni-Directional Fabrics

product1The Uni-Directional Fabrics is produced from model 35 continuous carbon fiber tow. Unique fiber spreading techniques are utilized to obtain a wide range of UD fabric weights for a varied set of composite part applications. Quick composite part build-up is cost effectively achieved with our diverse weight range of low-cost carbon fabric products.

Material Overview GE 150 GE 200 GE 300 GE 400 GE 500 GE 600 GE 900V
0° Carbon Fiber 458 200 309 403 500 600 865
90° Glass dtex 10 10 10 10 10 10
Polyester Vell 30
Polyester Stitch 6 6 6 6 6 6 5
Binder Resin Powder 8 8 8 8
Total Fabric Weight 182 g/mq 224 g/mq 333 g/mq 419 g/mq 516 g/mq 624 g/mq 900 g/mq
Fabric Construction GE 150 GE 200 GE 300 GE 400 GE 500 GE 600 GE 900V
Stitch Length 3.6 mm 3.6 mm 3.6 mm 3.6 mm 3.6 mm 3.6 mm 5.5 mm
Stitch Pattern Tricot Tricot Tricot Tricot Tricot Tricot 1\2 Tricot
Dry Thickness 0.4 mm 0.44 mm 0.57 mm 0.66 mm 0.76 mm 0.9 mm 1.25 mm
Roll Width 30 cm – 61 cm – 122 cm 30 cm – 61 cm – 122 cm 30 cm – 61 cm – 122 cm 30 cm – 61 cm – 122 cm 30 cm – 61 cm – 122 cm 30 cm – 61 cm – 122 cm 122cm
Roll Length 100 mt 100 mt 100 mt 100 mt 50mt 50mt 30mt
Material Overview GE 150 GE 200 GE 300 GE 400 GE 500 GE 600 GE 900V
Tensile Strength 4,137 MPa – 600ksi 4,137 MPa – 600ksi 4,137 MPa – 600ksi 4,137 MPa – 600ksi 4,137 MPa – 600ksi 4,137 MPa – 600ksi 4,137 MPa – 600ksi
Tensile Modulus 240 GPa – 35 msi 240 GPa – 35 msi 240 GPa – 35 msi 240 GPa – 35 msi 240 GPa – 35 msi 240 GPa – 35 msi 240 GPa – 35 msi
Fiber Diameter 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils 7.2 microns – 0.283 mils
Carbon Content 95 % 95 % 95 % 95 % 95 % 95 % 95 %